Dipped Nylon/Polyester Tyre Cord Fabric is main reinforcement and keep-shape material for rubber and tyre.
They have such distinguish features like as high breaking strength, excellent impact resistance, high fatigue-proof strength and good adhesive strength with rubber. it is widely used in the reinforcement for rubber tyres,
conveyor belts, hoses, flexible oil tanks for military purpose, fishing net ect.We can supply Dipped Nylon 6,
Nylon66 and Polyester Tyre Cord Fabric.

Dipped Nylon/Polyester Tyre Cord Fabric advantage :

1.High strength at break

2.Good adhesive strength

3.High anti-fatigue strength

4.Excellent impact resistance

5.Good bearing performance

THE SPECIFICATIONS OF DIPPED STD POLYESTER TIRE CORD FABRIC

 

THE SPECIFICATIONS OF DIPPED STD POLYESTER TIRE CORD FABRIC

 

ITEMSUNITE1000D/21300D/21000D/31500D/22000D/21300D/31500D/3
(1100dtex/2)(1440dtex/2)(1100dtex/3)(1670dtex/2)(2200dtex/2)(1440dtex/3)(1670dtex/3)
Breaking Stength (min)N/end140180205205280260305
Elongation at 44.1N%4.5+1.0
Elongation at 58.0N%4.5+1.0
Elongation at 66.6N%4.5+1.04.5+1.0
Elongation at 88.2N%4.5+1.04.5+1.0
Elongation at 100N%4.5+1.0
Adhension(H-test)(min)N/Cm125135140140170165180
Breaking strength

difference(max)

%4444444
Breaking elongation difference(max)%5555555
Dip pick up%3.5+13.5+13.5+13.5+13.5+13.5+13.5+1
Breaking elongation  (Min.)%15+/-215+/-215+/-215+/-215+/-215+/-215+/-2
Diametermm0.56+0.030.61+0.030.66+0.030.66+0.030.75+0.030.74+0.030.81+0.03
TwistPingle twist(Z)T/10cm45+1.540+1.537+1.537+1.533+1.533+1.531+1.5
Ply twist(S)45+1.540+1.537+1.537+1.533+1.533+1.531+1.5
Hot air shrinkage

177℃×2min x 0.05CN/dtex (max)

%3333333
Elongation @ Breaking of weft yarn (Min)%120120120120120120120

 

THE SPECIFICATIONS OF DIPPED HMLS POLYESTER TIRE CORD FABRIC

 

ITEMSUNITE1000D/21300D/21000D/31500D/22000D/21300D/31500D/3
(1100dtex/2)(1440dtex/2)(1100dtex/3)(1670dtex/2)(2200dtex/2)(1440dtex/3)(1670dtex/3)
Breaking Stength (min)N/end140180205205270260305
Elongation at 44.1N%4.5+1.0
Elongation at 58.0N4.5+1.0
Elongation at 66.6N4.5+1.04.5+1.0
Elongation at 88.2N%4.5+1.04.5+1.0
Elongation at 100N%4.5+1.0
Adhension(H-test)(min)N/Cm125135140140170165180
Breaking strength difference(max)%4444444
Breaking elongation difference(max)%5555555
Dip pick up%3.5+13.5+13.5+13.5+13.5+13.5+13.5+1
Breaking elongation (min)%14141414141414
Diametermm0.56+0.030.61+0.030.66+0.030.66+0.030.75+0.030.74+0.030.81+0.03
TwistPingle twist(Z)T/10cm45+1.540+1.537+1.537+1.533+1.533+1.530+1.5
Ply twist(S)45+1.540+1.537+1.537+1.533+1.533+1.530+1.5
Hot air shrinkage

177℃×2min x 0.05CN/dtex (max)

%2222222
Elongation @ Breaking of

weft yarn (Min)

%120120120120120120120

 

THE SPECIFICATIONS OF DIPPED NYLON-66 TIRE CORD FABRIC

ITEMUNIT840D/21260D/21260D/31680D/21890D/2
930dtex/21400dtex/21400dtex/31870dtex/22100dtex/2
Breaking Stength (min)N/end137.2215.6313.6284.2313.6
Elongation at 44.1N%8.5±0.6
Elongation at 66.6N%8.5±0.6
Elongation at 88.2N%8.5±0.6
Elongation at 100N%9±0.89±0.6
Adhension(H-test)(min)N/Cm107.8137.2156.8156.8156.8
Dip pick up%3.5+/-1.53.5+/-1.53.5+/-1.53.5+/-1.53.5+/-1.5
Breaking elongation%22.5+/-222.5+/-222+/-222.5+/-222+/-2
Diametermm0.53+/-0.030.65+/-0.030.78+/-0.030.74+/-0.030.78+/-0.03
TwistPingle twist(Z)T/10cm46+/-1.539+/-232+/-1.532+/-1.532+/-1.5
Ply twist(S)46+/-1.537+/-232+/-1.532+/-1.532+/-1.5
Hot air shrinkage 150C×30min(max)%555.555.5

 

THE SPECIFICATIONS OF DIPPED NYLON-6 TIRE CORD FABRIC

ITEMUNIT1890D/21260D/31680D/21260D/2840D/2
2100dtex/21400dtex/31870dtex/21400dtex/2930dtex/2
Breaking Stength (min)N/end305305269.5205.8132.3
Elongation at 44.1N%8±1.0
Elongation at 66.6N%8±1.0
Elongation at 88.2N%8±1.0
Elongation at 100N%8±1.08±1.0
Adhension(H-test)(min)N/Cm150150137.2117.698
Breaking strength difference(max)%44444
Breaking elongation difference(max)%66666
Dip pick up%3.5+/-1.53.5+/-1.53.5+/-1.53.5+/-1.53.5+/-1.5
Breaking elongation%23+/-223+/-222+/-222+/-222+/-2
Diametermm0.78+/-0.040.78+/-0.040.75+/-0.040.65+/-0.040.55+/-0.04
TwistPingle twist(Z)T/10cm32+/-232+/-233+/-1.537+/-1.546+/-1.5
Ply twist(S)32+/-232+/-233+/-1.537+/-1.546+/-1.5
Hot air shrinkage 150C×30min(max)%88888