Chafer Fabric 1260D/1x1260D/1

Dipped chafer fabric has quite high breaking strength and good adhesion. Wildly used in the tire bead. At the same time, due to its mesh construction, it’s also widely used in rubber board and rubber tubs etc    


Description:
Dipped chafer fabric for tire / rubber hoses
Dipped chafer fabric has quite high breaking strength and good adhesion. Wildly used in the tire bead. At the same time, due to its mesh construction, it’s also widely used in rubber board and rubber tubs etc. Standard products mainly made of nylon 6, nylon 66 and polyester. And we can always produce with different material and requirements.
Characteristics: 
High strength and thin:
Use only high strength industrial yarn to ensure the quality of the fabric, especially good at making monofilament chafer fabrics and multifilament chafer fabrics, which makes the fabric more thin and gaining more strength and longer life at the same time.
Plain mesh construction and high adhesion:
Due to the construction of plain woven mesh, the fabric allows all kinds of different rubber or chemicals to go through a combine together, which ensure the adhesion and strength at the same for the final products.
Applications:
Widely used in side parts of all kinds of tires (especially high speed tires)
Widely used in all kinds of rubber plant, rubber tubes and framework material for non-rubber products.
Specification:
420D/1x420D/1
450D/1x450D/1
840D/1x840D/1
1260D/1x1260D/1
1000D/1x1000D/1
1000D/10x1000D/10
We can supply all kinds of leno fabric as customer’s requirement.    

ITEMUNIT420D/1 x 420D/1450D/1 x 450D/1840D/1 x 840D/1840D/1 x 840D/11260D/1 x1260D/11260D/1 x 1260D/1
contentnylon 6nylon 6nylon 6nylon 66nylon 6nylon 66
weft breaking strengthN/end≥20≥30≥69≥71≥103≥105
Warp breaking strengthN/end≥20≥28≥67≥68≥100≥102
Adhesion ≥kg /inch≥20≥20≥20≥20≥20≥20
Dip pick up%3±1.53±1.511±311±311±311±3
Water content%1.51.51.51.51.51.5
Weft elongation at break%30±530±530±530±530±530±5
Warp elongation at break%25±525±525±525±525±525±5
Thicknessmm0.5±0.050.5±0.070.52±0.070.52±0.070.65±0.070.65±0.07
Weft shrinkage in hot air%≤2.0≤2.0≤2.0≤2.0≤2.0≤2.0
Warp shrinkage in hot air%≤3.0≤3.0≤3.0≤3.0≤3.0≤3.0
Weft densityend/inchbased on costomer's requestbased on costomer's requestbased on costomer's requestbased on costomer's requestbased on costomer's requestbased on costomer's request
Warp densityend/inchbased on costomer's requestbased on costomer's requestbased on costomer's requestbased on costomer's requestbased on costomer's requestbased on costomer's request
Widthcm100-150100-150100-150100-150100-150100-150